I-G10 Insulating Glass Epoxy Laminate
Ubukhulu obujwayelekile: 0.5 ~ 100mm
Usayizi ojwayelekile: 1020×2040mm
Indwangu ye-elekthronikhi ye-alkali engenawo ingilazi yengilazi ifakwe ku-epoxy resin engenisiwe, futhi yengezwe nezinqamuleli zomlilo ezihambisanayo, izinto ezinamathelayo nezinye izithasiselo, futhi zicutshungulwe ngokucindezela okushisayo.Ibanga le-Flame retardant UL94-VO grade, izakhiwo ezinhle zemishini emazingeni okushisa aphezulu, ukusebenza kahle kokucubungula nokusebenza kokufakelwa.
Isicelo sebhodi le-G10 epoxy: sisetshenziswa njengezingxenye zesakhiwo ezivikelayo ezimotweni nasezintweni zikagesi, njengezinqamuli zesekethe, ama-switch cabinets, ama-transformer, ama-DC motors, izixhumi ze-AC, izinto zikagesi ezingaqhumi nezinye izinto zikagesi.
Cha. | Izinto | Iyunithi | Inani Elijwayelekile | Umphumela wokuhlolwa |
1 | Amandla e-Flexural perpendicular to laminations | I-MPa | I-GB/T1303.4-2009 | ≥340 |
2 | Ukugoba i-modulus elastic | I-MPa | I-GB/T1303.4-2009 | / |
3 | Amandla we-Notch Impact ahambisana ne-lamination (i-charpy) | kJ/m2 | I-GB/T1303.4-2009 | ≥33 |
4 | Amandla aqinile | I-MPa | I-GB/T1303.4-2009 | / |
5 | Amandla e-Dielectric perpendicular to ama-laminations (emafutheni angu-20±2℃) | KV/mm | I-GB/T1303.4-2009 | ≥11.4 |
6 | I-voltage yokuhlukaniswaihambisana ne-lamination (emafutheni90±2℃) | KV | I-GB/T1303.4-2009 | ≥35 |
7 | 1 MHz isici sokulahlekelwa | / | I-GB/T1303.4-2009 | / |
8 | Ukumelana ne-insulation kufakwe emanzini | MΩ | I-GB/T1303.4-2009 | ≥5x10000 |
9 | I-CTI | / | I-GB/T 4207-2012 | / |
10 | Ukumuncwa kwamanzi | mg | I-GB/T 1303.4-2009 | ≤27 |
11 | Ukuminyana | g/cm3 | I-GB/T 1303.4-2009 | / |